Reliability analysis and life prediction of HK40 steel during high-temperature exposure

Published:2006-10 Issue:10 Volume:83 Page:730-735
ISSN:0308-0161
Container-title:International Journal of Pressure Vessels and Piping
language:en
Short-container-title:International Journal of Pressure Vessels and Piping

Author:

Xing Li,Zhao Jie,Shen Fu-zhong,Feng Wei

Publisher

Elsevier BV

Subject

Mechanical Engineering,Mechanics of Materials,General Materials Science

Reference22 articles.

1. A study on the prediction of remaining life and ageing of material for pressurized tubes of industrial furnace operated at elevated temperature;Shu-Ho;Int J Pressure Vessels Piping,1996

2. Assessment of damage and life prediction of austenitic stainless steel under high temperature creep–fatigue interaction condition;Soo Woo;Mater Sci Eng,2002

3. An evaluation of multi-axial fatigue life assessment methods for engineering components;Das;Int J Pressure Vessels Piping,1999

4. Particle-coarsening, σ0 and tertiary creep;Dyson;Acta Metall,1983

5. Use of CDM in materials modeling and component creep life prediction;Brian;J Pressure Vessel Technol,2000

Cited by 17 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Material Degradation Analysis and Reliability Assessment of Residual Life for Service-Exposed Reformer Tubes;Journal of Materials Engineering and Performance;2020-08

2. Creep failure in a threshold-activated dynamics: Role of temperature during a subcritical loading;Physical Review Research;2020-04-29

3. Effects of Cr Reduction on High-Temperature Strength of High-Ni Austenitic Cast Steels Used for High-Performance Turbo-chargers;Metallurgical and Materials Transactions A;2018-07-03

4. Solidification microstructure formation in HK40 and HH40 alloys;International Journal of Minerals, Metallurgy, and Materials;2016-04

5. Damage Analysis of Service Exposed Reformer Tubes in Petrochemical Industries;High Temperature Materials and Processes;2014-06-01