Fracture mechanics evaluation of cast duplex stainless steel after thermal aging

Published:1999-07 Issue:2 Volume:191 Page:255-261
ISSN:0029-5493
Container-title:Nuclear Engineering and Design
language:en
Short-container-title:Nuclear Engineering and Design

Author:

Tujikura Yonezou,Urata Shigeru

Publisher

Elsevier BV

Subject

Mechanical Engineering,Waste Management and Disposal,Safety, Risk, Reliability and Quality,General Materials Science,Nuclear Energy and Engineering,Nuclear and High Energy Physics

Reference8 articles.

1. Chopra, O.K., 1993 Long-term embrittlement of cast duplex stainless steel in LWR systems. Semiannual Report, April–September 1992. NUREG/CR-4744, ANL-93/11.

2. Chopra, O.K., Shack, W.T., 1992. Evaluation of aging degradation of structural components. Proceedings of the Aging Research Information Conference, NUREG/CP-0122.

3. Chopra, O.K., Shack, W.J., 1994. Assessment of thermal embrittlement of cast stainless steels. NUREG/CR-6177, ANL-94/2.

4. Chopra, O.K. et al., 1984. Long-term embrittlement of cast duplex stainless steel in LWR systems. Annual Report, October 1982–September 1983. NUREG/CR-3857, ANL-84-44.

5. Chung, H.M., Chopra, O.K., 1987.Long-term-aging embrittlement of cast austenitic stainless steels—mechanism and kinetics. Winter Annual Meeting of ASME MPC-vol. 26, PVP-vol. 32, 17.

Cited by 15 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Effect of thermal aging on the environmental assisted cracking behavior of 308L weld metal in high temperature water;Corrosion Science;2023-02

2. Evaluation of thermal aging activation energies based on multi-scale mechanical property tests for an austenitic stainless steel weld beads;Materials Science and Engineering: A;2022-02

3. Microstructure evolution and mechanical behavior of a lean duplex stainless steel aged at 475oC;Materials Science and Engineering: A;2021-04

4. Effect of heat input on austenite microstructural evolution of simulated heat affected zone in 2205 duplex stainless steel;Journal of Iron and Steel Research International;2018-09-24

5. Passive film properties of Z3CN20.09M duplex stainless steel aged for different times;Materials and Corrosion;2018-02-27