Retardation of crack growth in an aluminium alloy using a thermomechanical conditioning cycle-Reference-Cited by-同舟云学术

Retardation of crack growth in an aluminium alloy using a thermomechanical conditioning cycle

Published:1998-01 Issue:2 Volume:59 Page:215-224
ISSN:0013-7944
Container-title:Engineering Fracture Mechanics
language:en
Short-container-title:Engineering Fracture Mechanics

Author:

Ibrahim R.N,Sayers R.S.D,Ischenko D

Publisher

Elsevier BV

Subject

Mechanical Engineering,Mechanics of Materials,General Materials Science

Reference13 articles.

1. Establishing KIc from eccentrically fatigue cracked small circumferentially grooved cylindrical specimens;Ibrahim;Int. J. Fracture,1988

2. Ibrahim, R. N. and Lam, Y. C., Investigation of the apparent fracture toughness improvement technique for aluminium 6351-T6. In Proc. SIEF, Fifth Australian Aeronautical Conference, Melbourne, 1993, pp. 505–508

3. Improvement of the apparent fracture toughness of an aluminium alloy;Lam;Fatigue Fract. Engng Mater. Struct.,1994

4. The effect of intermittent heating on fatigue crack growth;Lam;Theor. Appl. Fracture Mech.,1993

5. The effect of simultaneous overload and spot heating on crack retardation in fatigue;Lam;Engng Fracture Mech.,1993

Cited by 6 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Review of Residual Stress Modification Techniques for Extending the Fatigue Life of Metallic Aircraft Components;APPL MECH REV;2015

2. Retardation of fatigue crack growth in aircraft aluminium alloys via laser heating – Experimental proof of concept;Materials Science and Engineering: A;2012-06

3. Fracture toughness for CNT specimens from numerically obtained critical CTOD values;Theoretical and Applied Fracture Mechanics;2009-08

4. Using Thermomechanical Conditioning Cycles to Improve Fracture Toughness of Low Carbon Steel;Metallurgical and Materials Transactions A;2009-03-11

5. Thermomechanical Manipulation of Crack-Tip Stress Field for Resistance to Stress Corrosion Crack Propagation;Metallurgical and Materials Transactions A;2008-10-23