Calcium–magnesium–alumino-silicate (CMAS) degradation of EB-PVD thermal barrier coatings: Characterization of CMAS damage on ex-service high pressure blade TBCs-Reference-Cited by-同舟云学术

Calcium–magnesium–alumino-silicate (CMAS) degradation of EB-PVD thermal barrier coatings: Characterization of CMAS damage on ex-service high pressure blade TBCs

Published:2012-09 Issue: Volume:208 Page:39-45
ISSN:0257-8972
Container-title:Surface and Coatings Technology
language:en
Short-container-title:Surface and Coatings Technology

Author:

Vidal-Setif M.H.,Chellah N.,Rio C.,Sanchez C.,Lavigne O.

Funder

French Defence Research Organization (DGA)

Publisher

Elsevier BV

Subject

Materials Chemistry,Surfaces, Coatings and Films,Surfaces and Interfaces,Condensed Matter Physics,General Chemistry

Reference21 articles.

1. Deposition of Volcanic Materials in the Hot Sections of Two Gas Turbine Engines

2. International SAMPE Metals Conference, October 20–22;Smialek,1992

3. Degradation of Thermal-Barrier Coatings at Very High Temperatures

4. Role of environment deposits and operating surface temperature in spallation of air plasma sprayed thermal barrier coatings

Cited by 107 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Degradation of LaPO4-8YSZ composite thick thermal barrier coatings by molten calcium-magnesium-aluminosilicate;Journal of the European Ceramic Society;2025-02

2. Cubic fluorite-based lanthanum cerium oxide thermal barrier top-coat fabrication, properties, and performance: Present status and prospects;Journal of the European Ceramic Society;2024-12

3. CMAS corrosion characteristics of YSZ and Al2O3-YSZ thermal barrier coatings at 1250 °C–1350 °C;Journal of the European Ceramic Society;2024-12

4. Understanding and Modeling CMAS and Thermal Barrier Coating Interaction Under Thermal Gradients;High Temperature Corrosion of Materials;2024-09-14

5. Cracking mechanism of CMAS-corroded thermal barrier coatings based on a coupled thermo-chemo-mechanically phase-field fracture model;European Journal of Mechanics - A/Solids;2024-09