The effect of crack branching on the residual lifetime of machine components containing stress corrosion cracks

Published:1985-01 Issue:8-9 Volume:25 Page:745-756
ISSN:0010-938X
Container-title:Corrosion Science
language:en
Short-container-title:Corrosion Science

Author:

Magdowski Ruth M.,Uggowitzer Peter J.,Speidel Markus O.

Publisher

Elsevier BV

Subject

General Materials Science,General Chemical Engineering,General Chemistry

Reference15 articles.

1. Proc. International Symposium on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors;Speidel,1984

2. Application of Fracture Mechanics to Materials and Structures;Speidel,1984

3. Corrosion in Power Generating Equipment;Speidel,1983

4. J.E. Bertilsson, B. Scarlin and M.O. Speidel Integrity of Low-Pressure Steam Turbine Rotors in Stress Corrosion Environments Brown Boveri Review 3/4–84, pp. 169–174, Zurich.

5. General Electric Nuclear S.C.C. Experience, Contribution to EPRI Steam Turbine Disc Integrity Seminar;Timo,1983

Cited by 5 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Crack branching behavior and amorphous film formation mechanism during SCC expanding test for multi-layers weld metal of NiCrMoV steels;Materials & Design;2022-04

2. Ultrasonic Pulsating Water Jet Peening: Influence of Pressure and Pattern Strategy;Materials;2021-10-13

3. Two-Dimensional Stress Corrosion Cracking Model for Reactor Structural Materials;Journal of Power and Energy Systems;2008

4. The stress corrosion cracking of as-quenched 4340 and 3.5NiCrMoV steels under stress rate control in distilled water at 90°C;Corrosion Science;1993-09

5. Thermal shock experiments on the HDR pressure vessel;Nuclear Engineering and Design;1991-10