The effect of slow plastic and elastic straining on sulphide stress cracking and hydrogen embrittlement of 3.5% Ni steel and API 5L X60 pipeline steel-Reference-Cited by-同舟云学术

The effect of slow plastic and elastic straining on sulphide stress cracking and hydrogen embrittlement of 3.5% Ni steel and API 5L X60 pipeline steel

Published:1987-01 Issue:10-11 Volume:27 Page:1153-1167
ISSN:0010-938X
Container-title:Corrosion Science
language:en
Short-container-title:Corrosion Science

Author:

Erlings J.G.,de Groot H.W.,Nauta J.

Publisher

Elsevier BV

Subject

General Materials Science,General Chemical Engineering,General Chemistry

Reference9 articles.

1. Stress Corrosion Research;Parkins,1979

2. The Theory of Stress Corrosion Cracking in Alloys;Engell,1971

3. Stress Corrosion Research;Parkins,1979

4. Stress Corrosion Cracking of Low Strength, Low Alloy Nickel Steels in Sulfide Environments

5. Hydrogen in Steel;Smialowski,1962

Cited by 23 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Evaluation of the “nickel effect” in sulfide stress cracking of low alloy steels;International Journal of Hydrogen Energy;2024-05

2. The Role of Nickel in Low Alloy Steels Exposed to H2S Containing Environments. Part II: Effect of the Electrochemical Potential and Stress Level on Trench Formation;Corrosion;2023-11-07

3. The Role of Nickel in Low Alloy Steels Exposed to H2S-Containing Environments. Part I: Trench Formation at the Open-Circuit Potential;Corrosion;2023-10-11

4. Effect of Anodic Polarization on the Susceptibility of AA6111 Automotive Sheet to Stress Corrosion Cracking;Corrosion;2023-09-20

5. Pits formation and stress corrosion cracking behavior of Q345R in hydrofluoric acid;Corrosion Science;2020-04