A new understanding of intergranular stress corrosion cracking resistance of pipeline steel through grain boundary character and crystallographic texture studies-Reference-Cited by-同舟云学术

A new understanding of intergranular stress corrosion cracking resistance of pipeline steel through grain boundary character and crystallographic texture studies

Published:2009-01 Issue:1 Volume:51 Page:119-128
ISSN:0010-938X
Container-title:Corrosion Science
language:en
Short-container-title:Corrosion Science

Author:

Arafin M.A.,Szpunar J.A.

Publisher

Elsevier BV

Subject

General Materials Science,General Chemical Engineering,General Chemistry

Reference45 articles.

1. Federal Power Commission, Bureau of Natural Gas, Washington DC, Final staff report on investigation of Tennessee Gas Transmission Company Pipeline No. 100-1 failure near Natchitoches, Louisiana, March 4, 1965, Docket No. CP65-267.

2. Gas pipeline failures: Australian experience;Kentish;Br. Corros. J.,1985

3. Review of stress corrosion cracking of pipeline steels in and “high” pH solutions low;Fang;Mater. Sci.,2003

4. Generation of stress corrosion cracking environments at pipeline surfaces;Charles;Corrosion,1995

5. Mechanism of high-pH and near-neutral-pH SCC of underground pipelines;Beavers;J. Offshore Mech. Arct. Eng.,2001

Cited by 218 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Transverse crack micromechanisms in high-strength steel weld metal with microstructure heterogeneity under hydrogen-containing environment;Materials Science and Engineering: A;2024-11

2. Fracture properties of austenitic stainless steel grain boundaries oxidized in PWR environment;Acta Materialia;2024-10

3. Investigating the hydrogen diffusion and cracking susceptibility of pipeline steels after various heat treatments;Engineering Failure Analysis;2024-07

4. On the corrosion of additively manufactured Inconel 718 with different crystallographic orientations exposed to 3.5% NaCl;Additive Manufacturing;2024-07

5. Failure Analysis of Leakage in the Decomposition Tank of Bayer Process for Producing Alumina;Journal of Failure Analysis and Prevention;2024-06-04