The effect of sulphur on the carburization of three Fe-19Ni-13Cr alloys with various Al additions at 900 °C in oxygen-contaminated CH 4 -H 2 -H 2 S atmospheres-Reference-Cited by-同舟云学术

The effect of sulphur on the carburization of three Fe-19Ni-13Cr alloys with various Al additions at 900 °C in oxygen-contaminated CH 4 -H 2 -H 2 S atmospheres

Published:2016-11 Issue: Volume:112 Page:94-109
ISSN:0010-938X
Container-title:Corrosion Science
language:en
Short-container-title:Corrosion Science

Author:

Liu S.,Shen J.,Wu X.F.,Li H.,Niu Y.

Funder

NSFC project

Publisher

Elsevier BV

Subject

General Materials Science,General Chemical Engineering,General Chemistry

Reference29 articles.

1. Effect of pre-oxidization on the cyclic coking and carburizing resistance of HP40 alloy: with and without yttrium modification;Ma;Corros. Sci.,2013

2. Effect of yttrium on the coking behavior of Fe-based superalloy in heavy hydrocarbon;Li;Corros. Sci.,2015

3. Fe-base alloys in CH4/H2 carburizing gas mixtures;Yin;Mater. High Temp.,2004

4. Performance of Cr oxide coatings on 304 steel against metal dusting;Melo-Maximo;Surf. Coat. Technol.,2013

5. Role of PVD oxide coatings on HK40 cast steel during short and long exposure to C-rich atmospheres;Salas;Mater. Charact.,2013

Cited by 3 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Influence of fuel combustion on the corrosion behavior of pipeline steels in fire flooding technology;npj Materials Degradation;2022-03-22

2. Establishing the Cause of Failure in a Secondary Reformer Nozzle in an Ammonia Plant;Journal of Failure Analysis and Prevention;2021-06-23

3. Corrosion of Fe-Ni-Cr alloys with various aluminum additions in a carburizing-oxidizing atmosphere at 900 °C;Corrosion Science;2018-05