Determination of the critical hydrogen concentration for delayed fracture of high strength steel by constant load test and numerical calculation-Reference-Cited by-同舟云学术

Determination of the critical hydrogen concentration for delayed fracture of high strength steel by constant load test and numerical calculation

Published:2006-08 Issue:8 Volume:48 Page:2189-2202
ISSN:0010-938X
Container-title:Corrosion Science
language:en
Short-container-title:Corrosion Science

Author:

Wang Maoqiu,Akiyama Eiji,Tsuzaki Kaneaki

Publisher

Elsevier BV

Subject

General Materials Science,General Chemical Engineering,General Chemistry

Reference25 articles.

1. ASTM E 1681-95: Standard test method for determining a threshold stress intensity factor for environment-assisted cracking of metallic materials under constant load.

2. Evaluation Method of Delayed Fracture Property of High Strength Steels

3. Hydrogen induced delayed fracture of ultrafine grained 0.6% O steel with dispersed oxide particles

Cited by 137 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Experimental and Fractographic Study of the Hydrogen‐Induced Cracking of 45CrNiMoVA Martensitic Advanced High‐Strength Steel;steel research international;2024-08-29

2. Failure of a high-pressure flash gas pipeline from coal coke gasification to the cleaning section due to hydrogen-induced cracking;Canadian Metallurgical Quarterly;2024-08-21

3. Numerical analysis of the fully-coupled continuum cohesive modeling on the hydrogen-assisted degradation behavior in high-strength steel;Materials Today Communications;2024-08

4. Effect of barnacle on the cathodic protection of high-strength steel and its potential risk related to hydrogen permeation;Corrosion Science;2024-07

5. Enhancement of hydrogen embrittlement resistance in 310S austenitic stainless steel through ribbon-like δ-ferrite;Corrosion Science;2024-06