A simple model for slow strain rate and constant load corrosion tests of austenitic stainless steel in acid aqueous solution containing sodium chloride-Reference-Cited by-同舟云学术

A simple model for slow strain rate and constant load corrosion tests of austenitic stainless steel in acid aqueous solution containing sodium chloride

Published:2008-10 Issue:10 Volume:50 Page:2858-2866
ISSN:0010-938X
Container-title:Corrosion Science
language:en
Short-container-title:Corrosion Science

Author:

da Costa-Mattos H.S.,Bastos I.N.,Gomes J.A.C.P.

Publisher

Elsevier BV

Subject

General Materials Science,General Chemical Engineering,General Chemistry

Reference15 articles.

1. Stress corrosion cracking of gas pipelines – Effect of surface roughness orientations and flattening;Kentish;Corros. Sci.,2007

2. Stress-Corrosion Mechanisms;Newman,1995

3. An inconsistency in “film rupture model” of stress corrosion cracking;Gutman;Corros. Sci.,2007

4. Electrochemical impedance and current fluctuation analysis during slow strain rate test of a UNS S30400 stainless steel in low pH media;Bastos;J. Braz. Chem. Soc.,2005

5. SCC evaluation of type 304 and 316 austenitic stainless steels in acidic chloride solutions using the slow strain rate technique;Nishimura;Corros. Sci.,2004

Cited by 62 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Cyclic inelastic behaviour of a bonded patch repair system used for pipes with through-wall corrosion damage;Engineering Failure Analysis;2024-10

2. In vitro calibration and in vivo validation of phenomenological corrosion models for resorbable magnesium-based orthopaedic implants;Acta Biomaterialia;2024-05

3. Cyclic Failure Behaviour of a Bonded Metal Patch Repair System Used for Pipes with Through-Wall Corrosion Damage;2024

4. Application of Artificial Intelligence at All Stages of Bone Tissue Engineering;Biomedicines;2023-12-28

5. Numerical Simulation of Dynamic Degradation and Fatigue Damage of Degradable Zinc Alloy Stents;Journal of Functional Biomaterials;2023-11-15