Corrosion fatigue damage mechanism and life evaluation of Inconel Alloy 690TT steam generator tube in high temperature pressurized water-Reference-Cited by-同舟云学术

登录注册会员服务联系我们

Corrosion fatigue damage mechanism and life evaluation of Inconel Alloy 690TT steam generator tube in high temperature pressurized water

Published:2023-03 Issue: Volume:212 Page:110953
ISSN:0010-938X
Container-title:Corrosion Science
language:en
Short-container-title:Corrosion Science

Author:

Li Z.H.,Lu Y.H.,Hong C.,Zhao Y.G.,Han Y.M.,Shoji T.

Funder

Beijing Municipal Science and Technology Commission

Publisher

Elsevier BV

Subject

General Materials Science,General Chemical Engineering,General Chemistry

Reference50 articles.

1. Statistical modeling of fatigue crack growth rate in Inconel alloy 600;Al-Rubaie;Inter. J. Fatigue,2006

2. An investigation of the fatigue crack growth behavior of INCONEL 690;Young;Mater. Sci. Eng. A,2006

3. The effect of dissolved oxygen on fatigue behavior of alloy 690 steam generator tubes in borated and lithiated high temperature water;Tan;Corros. Sci.,2016

4. Effects of dissolved oxygen on corrosion fatigue cracking of Alloy 690(TT) in pressurized water reactor environments;Xiao;Inter. J. Fatigue,2015

5. Low cycle fatigue behavior of alloy 690 in simulated PWR water-effects of dynamic strain aging and hydrogen;Hong;Mater. Sci. Eng. A,2014

Cited by 6 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Effects of high-temperature and high-pressure immersion corrosion durations on the fretting tribo-corrosion behaviors of Inconel 690 alloy;Wear;2024-11

2. Thermal corrosion fatigue crack growth behavior and life prediction of 304SS pipeline structures in high temperature pressurized water;Engineering Failure Analysis;2024-06

3. Effects of dissolved hydrogen on corrosion fatigue crack growth behavior of 316LN stainless steel in high temperature pressurized water environment;Corrosion Science;2024-05

4. Effect of thermal aging on the low cycle fatigue behavior of Z3CN20.09M stainless steel in high-temperature pressurized water;Corrosion Science;2024-04

5. Effect of temperature on corrosion fatigue behavior of Inconel Alloy 690TT steam generator tube;Corrosion Science;2024-02

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线，采集、加工和组织学术论文而形成的新型学术文献查询和分析系统，可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容，当前同舟云学术共收录了国内外主流学术期刊6万余种，收集的期刊论文及会议论文总量共计约1.5亿篇，并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询！咨询电话：010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号京ICP备18003416号-3