Effects of temperature on stress corrosion cracking behavior of stainless steel and outer oxide distribution in cracks due to exposure to high-temperature water containing hydrogen peroxide-Reference-Cited by-同舟云学术

Effects of temperature on stress corrosion cracking behavior of stainless steel and outer oxide distribution in cracks due to exposure to high-temperature water containing hydrogen peroxide

Published:2014-01 Issue:1-3 Volume:444 Page:454-461
ISSN:0022-3115
Container-title:Journal of Nuclear Materials
language:en
Short-container-title:Journal of Nuclear Materials

Author:

Nakano Junichi,Sato Tomonori,Kato Chiaki,Yamamoto Masahiro,Tsukada Takashi,Kaji Yoshiyuki

Publisher

Elsevier BV

Subject

Nuclear Energy and Engineering,General Materials Science,Nuclear and High Energy Physics

Reference20 articles.

1. T. Okamura, A. Sakashita, T. Fukuda, H. Yamashita, T. Futami, in: Trans of the 17th Int. Conf. on Structural Mechanics in Reactor Technology, #WG01-1, 2003, p. 1.

2. Y. Wada, K. Ishida, M. Tachibana, in: Proc. of the 11th Int. Conf. Environmental Degradation of Materials in Nuclear Systems, 2003, p. 488.

3. Effects of Hydrogen Peroxide on Intergranular Stress Corrosion Cracking of Stainless Steel in High Temperature Water, (I)

4. Analysis of Oxide Film Formed on Type 304 Stainless Steel in 288°C Water Containing Oxygen, Hydrogen, and Hydrogen Peroxide

Cited by 3 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Effect of hydrogen charging on SCC of 2205 duplex stainless steel with varying microstructures in simulated deep-sea environment;Corrosion Science;2022-03

2. Failures and leak inspection techniques of tube-to-tubesheet joints: A review;Engineering Failure Analysis;2021-12

3. Corrosion behavior of ferritic FeCrAl alloys in simulated BWR normal water chemistry;Journal of Nuclear Materials;2021-03