Strain-induced corrosion cracking of low-alloy steels in LWR systems — case histories and identification of conditions leading to susceptibility-Reference-Cited by-同舟云学术

Strain-induced corrosion cracking of low-alloy steels in LWR systems — case histories and identification of conditions leading to susceptibility

Published:1986-02 Issue:3 Volume:91 Page:305-330
ISSN:0029-5493
Container-title:Nuclear Engineering and Design
language:en
Short-container-title:Nuclear Engineering and Design

Author:

Hickling J.,Blind D.

Publisher

Elsevier BV

Subject

Mechanical Engineering,Waste Management and Disposal,Safety, Risk, Reliability and Quality,General Materials Science,Nuclear Energy and Engineering,Nuclear and High Energy Physics

Reference40 articles.

1. Development of strain-rate testing and its implications;Parkins,1979

2. On the role of stress induced corrosion and corrosion fatigue in the formation of cracks in water wetted boiler components;Schoch,1972

3. Environmental aspects of carbon steel stress corrosion;Indig,1982

4. Effect of oxygen/temperature combinations on the stress corrosion susceptibility of SA 333-Gr6 carbon steel in BWR quality water;Ford,1982

5. Stress corrosion cracking of ASTM A508 C1 2 steel in oxygenated water at elevated temperatures;Choi;Corrosion,1982

Cited by 51 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Corrosion and Environmentally-Assisted Cracking of Carbon and Low-Alloy Steels;Comprehensive Nuclear Materials;2020

2. Environmentally-assisted cracking of carbon and low-alloy steels in light water reactors;Nuclear Corrosion;2020

3. Environmental degradation of fracture resistance in high-temperature water environments of low-alloy reactor pressure vessel steels with high sulphur or phosphorus contents;Corrosion Science;2019-07

4. Effect of dynamic strain ageing on environmental degradation of fracture resistance of low-alloy RPV steels in high-temperature water environments;Corrosion Science;2019-05

5. Contribution of research to the understanding and mitigation of environmentally assisted cracking in structural components of light water reactors;Corrosion Engineering, Science and Technology;2017-11-06