Formation mechanism and influence of white etching area on contact fatigue spalling of M50 bearing steel

Published:2022-09 Issue: Volume:139 Page:106273
ISSN:1350-6307
Container-title:Engineering Failure Analysis
language:en
Short-container-title:Engineering Failure Analysis

Author:

Hou Xue-Qin,Zhang Zheng,Liu Chang-Kui,Tao Chun-Hu

Publisher

Elsevier BV

Subject

General Engineering,General Materials Science

Reference43 articles.

1. Characterisation of white etching crack damage in wind turbine gearbox bearings;Bruce;Wear,2015

2. White structure flaking (WSF) in wind turbine gearbox bearings: effects of 'butterflies' and white etching cracks (WECs);Evans;Mater. Sci. Technol.,2012

3. H. Guo, J.Z. Lei, L.Z. Hu, Influencing factors of contact fatigue failure of rolling bearings and their research status, Failure Analysis and Prevention. 14(3)(2019)206-211.https://dx.doi.10.3969/j.issn.1673-6214.2019.03.013.

4. Dark etching regions under rolling contact fatigue: a review;Echeverri Restrepo;Mater. Sci. Technol.,2021

5. Electron microscopy investigations of microstructural alterations due to classical Rolling Contact Fatigue (RCF) in martensitic AISI 52100 bearing steel;Šmeļova;Int. J. Fatigue,2017

Cited by 16 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Investigation of white etching area at non-carbides origin in M50 bearing steel under rolling contact fatigue;Tribology International;2025-01

2. Fatigue failure mechanism of high-speed train bearing steel after long-term service;Engineering Failure Analysis;2024-11

3. High-Temperature Decomposition Mechanism of M₂C Primary Carbide in M50 Steel;ACTA METALL SIN;2024

4. Research on Multi-Directional Spalling Evolution Analysis Method for Angular Ball Bearing;Applied Sciences;2024-06-11

5. Influence mechanism of grinding surface quality of 20CrMnTi steel on contact failure;Scientific Reports;2024-06-11