Study on immersion corrosion behavior and mechanism of SDCM die steel for hot stamping-Reference-Cited by-同舟云学术

Study on immersion corrosion behavior and mechanism of SDCM die steel for hot stamping

Published:2022-07 Issue: Volume:137 Page:106235
ISSN:1350-6307
Container-title:Engineering Failure Analysis
language:en
Short-container-title:Engineering Failure Analysis

Author:

Jiang Bin,Zuo Pengpeng,Wu Xiaochun

Publisher

Elsevier BV

Subject

General Engineering,General Materials Science

Reference49 articles.

1. Advance on friction of stamping forming;Li;The International Journal of Advanced Manufacturing Technology,2018

2. Hot stamping of ultra-high strength steel parts;Mori;CIRP Ann.,2017

3. Crack Initiation Life of Materials Under Combined Pitting Corrosion and Cyclic Loading;Sriraman;J. Mater. Eng. Perform.,2010

4. T Lu. B, Luo. J. L. Crack initiation and early propagation of X70 steel in simulated near-neutral pH groundwater, 2006, 62(8): 723-731.

5. Initiation sites for cracks developed from pits in a shot-peened 12Cr martensitic stainless steel;Guo;Initiation sites for cracks developed from pits in a shot-peened 12Cr martensitic stainless steel,2017

Cited by 3 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Improving stress corrosion resistance and wear resistance of austenitic hot-stamping die steels via synergistic effects of shot peening and plasma nitriding;Surface and Coatings Technology;2024-02

2. Effects of soldering and wear of die-casting die during ejection: Surface roughness and casting temperature;Engineering Failure Analysis;2023-09

3. Research and Analysis of Out-of-Tolerance Problem in Mold Processing Based on Intelligence;Advances in Multimedia;2022-09-15