Failure analysis of a carbon steel screw under the service in the presence of hydrogen sulphide
Author:
Publisher
Elsevier BV
Subject
General Engineering,General Materials Science
Reference18 articles.
1. Effect of microstructure on the sulphide stress cracking susceptibility of a high strength pipeline steel;Ramírez;Corros Sci,2008
2. The influence of chemical composition and microstructure of API line pipe steels on hydrogen induced cracking and sulfide stress corrosion cracking;Carneiro;Mater Sci Eng, A,2003
3. Damage mechanisms affecting fixed equipment in the refining industry. American Petroleum Institute. API 571 RP; 2003. p. 5.41–5.44.
4. Quantitative fractography of 2205 duplex stainless steel after a sulfide stress cracking test;Klyk-Spyra;Mater Charact,2006
5. Effect of H2S on stress corrosion cracking and hydrogen permeation behaviour of X56 grade steel in atmospheric environment;Zheng;Corros Eng Sci Technol,2009
Cited by 10 articles. 订阅此论文施引文献 订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献
1. Fracture toughness evaluation of 1.4841 bolt subjected to simultaneous effects of creep and hydrogen embrittlement phenomena using small punch test: A case study in a superheater of a petrochemical unit;Engineering Failure Analysis;2023-02
2. Sulfide Stress Cracking of Offshore Gas Injection Header: A Case Study;Journal of Failure Analysis and Prevention;2021-10
3. Fracture failure analysis of the sacrificial anode protector in a water injection well;Engineering Failure Analysis;2020-05
4. Failure Analysis of Super Hard End Mill HSS-Co;Open Engineering;2019-07-26
5. Root cause of end mill cutting tool failure;AIP Conference Proceedings;2019
1.学者识别学者识别
2.学术分析学术分析
3.人才评估人才评估
"同舟云学术"是以全球学者为主线，采集、加工和组织学术论文而形成的新型学术文献查询和分析系统，可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容，当前同舟云学术共收录了国内外主流学术期刊6万余种，收集的期刊论文及会议论文总量共计约1.5亿篇，并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询！咨询电话：010-8811{复制后删除}0370
www.globalauthorid.com
TOP
Copyright © 2019-2024 北京同舟云网络信息技术有限公司 京公网安备11010802033243号 京ICP备18003416号-3