Abnormal creep property degradation in a directionally solidified superalloy DZ406 after suffering overheating-Reference-Cited by-同舟云学术

Abnormal creep property degradation in a directionally solidified superalloy DZ406 after suffering overheating

Published:2021-03 Issue: Volume:173 Page:110910
ISSN:1044-5803
Container-title:Materials Characterization
language:en
Short-container-title:Materials Characterization

Author:

Xing Weijie,Zhu Gang,Zuo Xinlang,Guo Xiaotong,Zhao Zhenbo,Xiao Hui,Zheng Zhen,Zhao Wenxia,Liu Changkui

Funder

National Key Research and Development Program of China

Publisher

Elsevier BV

Subject

Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science

Reference39 articles.

1. The Superalloys: Fundamentals and Applications;Reed,2008

2. Superalloys II: High-Temperature Materials for Aerospace and Industrial Power;Sims,1987

3. Academic committee of the superalloys CSM, in: China Superalloys Handbook, Standard press of China, Beijing, 2012, pp. 232–255.

4. S. Rani, A.K. Agrawal, V. Rastogi, Failure investigations of a first stage Ni-based super alloy gas turbine blade, Materials Today: Proceedings 5(1, Part 1) (2018) 477–486.

5. Failure analysis of gas turbine first stage blade made of nickel-based superalloy;Kolagar;Case. Stud. Eng. Fail. Anal.,2017

Cited by 18 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Pre-softening HIP treatment enabled crack-healing and superior mechanical properties for René 142 superalloy fabricated via laser powder bed fusion;Journal of Materials Science & Technology;2025-03

2. Effects of uncontrolled combustion in a power plant gas turbine on fracture surface features and microstructural evolutions of a nickel-based superalloy blades;Engineering Failure Analysis;2024-06

3. Solid dust induced roughening and overheating of TBC-coated superalloy;Journal of Materials Science & Technology;2024-05

4. The evolution of carbides during long-term creep/aging of nickel based superalloy K444;Journal of Materials Research and Technology;2024-01

5. Stress-induced influence on the evolution of γ′ phase in dendritic area during long-term stress aging at 900 °C in Ni-based superalloy K444;Materials Characterization;2024-01