Scanning Kelvin Probe Blister test measurements of adhesive delamination – Bridging the gap between experiment and theory-Reference-Cited by-同舟云学术

Scanning Kelvin Probe Blister test measurements of adhesive delamination – Bridging the gap between experiment and theory

Published:2017-03 Issue: Volume:73 Page:8-15
ISSN:0143-7496
Container-title:International Journal of Adhesion and Adhesives
language:en
Short-container-title:International Journal of Adhesion and Adhesives

Author:

Grothe R.,Liu Chen-Ni,Baumert M.,Hesebeck O.,Grundmeier G.

Funder

German Science Foundation

AiF within the “BestKleb” joint research cluster

Publisher

Elsevier BV

Subject

Polymers and Plastics,General Chemical Engineering,Biomaterials

Reference37 articles.

1. Adhesion and adhesives: science and technology;Kinloch,1987

2. Failure mechanisms in the boundary layer zone of metal/polymer systems;Brockmann,1984

3. Design of adhesive joints under humid conditions,2013

4. Pascoe JA, Alderliesten RC, Benedictus R. Methods for the prediction of fatigue delamination growth in composites and adhesive bonds. A critical review.

5. Williams G, McMurray HN Chromate inhibition of corrosion-driven organic coating delamination studied using a scanning Kelvin probe technique.

Cited by 10 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Interaction of interfacial debonding and under-film corrosion propagation at the edge of the blistering area of epoxy coating;Journal of Coatings Technology and Research;2023-03

2. Blistering of color coated steel: Use of broad ion beam milling to examine degradation phenomena and coating defects;Surface and Coatings Technology;2022-10

3. Electrolytic cleaning study of cold rolled steel using scanning Kelvin probe;Surface Engineering;2022-05-04

4. Prospect of Using Machine Learning-Based Microwave Nondestructive Testing Technique for Corrosion Under Insulation: A Review;IEEE Access;2022

5. Blister tests on thin-walled composite structures at different temperatures;International Journal of Adhesion and Adhesives;2021-10