A novel approach for quantifying hydrogen embrittlement using side-grooved CT samples-Reference-Cited by-同舟云学术

A novel approach for quantifying hydrogen embrittlement using side-grooved CT samples

Published:2022-04 Issue: Volume:265 Page:108324
ISSN:0013-7944
Container-title:Engineering Fracture Mechanics
language:en
Short-container-title:Engineering Fracture Mechanics

Author:

Laliberté-Riverin Simon^ORCID,Brochu Myriam

Funder

Consortium de Recherche et d’innovation en Aérospatiale au Québec

Natural Sciences and Engineering Research Council of Canada

Fonds de recherche du Québec – Nature et technologies

Publisher

Elsevier BV

Subject

Mechanical Engineering,Mechanics of Materials,General Materials Science

Reference53 articles.

1. Hydrogen, crack initiation, and delayed failure in steel;Johnson;Trans Metall Soc AIME,1958

2. The role of hydrogen and other interstitials in the mechanical behavior of metals;Troiano;Trans ASM,1960

3. The effect of baking and stress on the hydrogen content of cadmium plated high strength steels;Berman;Mater Perform,1985

4. Characteristics of hydrogen embrittlement, stress corrosion cracking and tempered martensite embrittlement in high-strength steels;Eliaz;Eng Fail Anal,2002

5. Internal hydrogen embrittlement of pre-cracked, cadmium-plated AISI 4340 high strength steel with sustained load tests and incremental step-loading tests;Laliberté-Riverin;Eng Fract Mech,2020

Cited by 5 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Proposal of new crack-tip-opening-displacement as a mechanical driving force of elastic-plastic fracture mechanics;Theoretical and Applied Fracture Mechanics;2023-12

2. Control and Application of Ultrahigh Hydrogen Flux in Materials;Plasma and Fusion Research;2023-08-17

3. Innovative Design of Residual Stress and Strain Distributions for Analyzing the Hydrogen Embrittlement Phenomenon in Metallic Materials;Materials;2022-12-19

4. Stiffness-based method to identify the threshold load of low hardness steels using the Incremental step loading test;Engineering Failure Analysis;2022-12

5. Critical hydrogen concentration for crack propagation in a CrMo steel: Targeted experiments for accurate numerical modelling;Engineering Fracture Mechanics;2022-10