The study of temperature and radiation induced degradation of cable polymers: A comparison between the mechanical properties of industrial and neat EPDM-Reference-Cited by-同舟云学术

The study of temperature and radiation induced degradation of cable polymers: A comparison between the mechanical properties of industrial and neat EPDM

Published:2016 Issue: Volume:2 Page:2405-2414
ISSN:2452-3216
Container-title:Procedia Structural Integrity
language:en
Short-container-title:Procedia Structural Integrity

Author:

Šarac T.,Quiévy N.,Gusarov A.,Konstantinović M.J.

Publisher

Elsevier BV

Subject

General Engineering,Energy Engineering and Power Technology

Reference21 articles.

1. Willan, A., Thue (Ed.), 2011. Electrical Power Cable Engineering, Third edition, CRC Press

2. A Short History of Rubber Cables;Zuidema;IEEE Electricsl Insulation Magazine,2011

3. Insulation Materials for Wire and Cable Insulation;Mead;Rubber Chemistry and Technology,2002

4. Radiochemical Aging of Ethylene-Propylene-Diene Monomer Elastomers. I. Mechanism of Degradation under Inert Atmosphere;Rivaton;Journal of Polymer Science Part A-Polymer Chemisrty,2004

5. Radiochemical Ageing of EPDM Elastomers. 2. Identification and Quantification of Chemical Changes in EPDM and EPR Films γ-irradiated under Oxygen Atmosphere;Rivaton;Nuclear Instruments and Methods in Physics Research B,2005

Cited by 12 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Effects of Climatic Aging on the Performance of EPDM Used in Power Cable Insulation;2024 IEEE 5th International Conference on Dielectrics (ICD);2024-06-30

2. Recent progress in the accelerated aging and lifetime prediction of elastomers : A review;Polymer Degradation and Stability;2023-08

3. Research on the effect of thermal fracture failure behavior on thermal friction of flexible cable;Tribology International;2022-12

4. Effect of temperature and aging duration on ethylene propylene diene monomer (EPDM) nonmetallic components used in caustic liquid waste transfer lines;Engineering Failure Analysis;2021-10

5. Constitutive modeling of elastomers during photo- and thermo-oxidative aging;Polymer Degradation and Stability;2021-09