Evolution of damage during the fatigue of 3D woven glass-fibre reinforced composites subjected to tension–tension loading observed by time-lapse X-ray tomography-Reference-Cited by-同舟云学术

Evolution of damage during the fatigue of 3D woven glass-fibre reinforced composites subjected to tension–tension loading observed by time-lapse X-ray tomography

Published:2016-03 Issue: Volume:82 Page:279-290
ISSN:1359-835X
Container-title:Composites Part A: Applied Science and Manufacturing
language:en
Short-container-title:Composites Part A: Applied Science and Manufacturing

Author:

Yu B.,Blanc R.,Soutis C.,Withers P.J.

Funder

EPSRC

China Scholarship Council

University Of Manchester

Publisher

Elsevier BV

Subject

Mechanics of Materials,Ceramics and Composites

Reference34 articles.

1. Evolution of failure mechanisms in 2D and 3D woven composite systems under quasi-static perforation;Baucom;J Compos Mater,2003

2. Low-velocity impact damage progression in woven E-glass composite systems;Baucom;Compos A Appl Sci Manuf,2005

3. Toughness properties of a three-dimensional carbon–epoxy composite;Guénon;J Mater Sci,1989

4. X-ray microtomography analysis of the damage micromechanisms in 3D woven composites under low-velocity impact;Seltzer;Compos A Appl Sci Manuf,2013

5. Lockup, chains and the delocalization of damage;Cox;J Mater Sci,1996

Cited by 86 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. A new progressive fatigue damage model for the three-dimensional braided composites subjected to locally-variable-amplitude loading;International Journal of Fatigue;2024-07

2. Influence of the mesostructure on the fatigue behaviour of textile composites;Composites Part A: Applied Science and Manufacturing;2024-06

3. Hygrothermal progressive damage in open-hole compression of composite laminates with aligned carbon nanotube interlaminar reinforcement studied by X-ray micro-computed tomography;Composites Part B: Engineering;2024-06

4. Online and Ex Situ Damage Characterization Techniques for Fiber-Reinforced Composites under Ultrasonic Cyclic Three-Point Bending;Polymers;2024-03-13

5. Assessment of low-velocity impact response of a hybrid carbon-aramid braided composite by algorithmic quantification of volumetric structures;Tomography of Materials and Structures;2024-03