Abstract
Background/Aim: The aim of this study is to compare the impact of CO 2 laser on traditional zirconia and translucent zirconia in terms of the bonding strength to resin cement. Material and Methods: In this in-vitro study 20 zirconia disks (10 mm diameter and 2 mm thickness) were assigned to two groups (n = 10). Group 1: 10 discs of traditional zirconia, Group 2: 10 discs of translucent zirconia, CO 2 lasers were used for pretreatment of zirconia surface, respectively. Dentinal disks were cemented on zirconia disk using dual-curing resin cement. Shear bond strength tests were performed at a crosshead speed of 1 mm/min after 24 h distilled water storage. Data was analyzed by T Student's test. Results: The means and standard deviations of shear bond strength values in Group 1, and Group 2 were 1.15, 0.38, 1.99 , 0.65 MPa respectively. Data showed that application of CO 2 laser resulted in a significant higher shear bond strength of resin cement to translucent zirconia ceramics (p < 0.05). Conclusions: Application of CO 2 laser treatment (3W) increases the bond strength to the resin cement of translucent zirconia compared to traditional zirconia.
Publisher
Centre for Evaluation in Education and Science (CEON/CEES)
Reference24 articles.
1. Denry I, Kelly JR (2008). "State of the art of zirconia for dental applications". Dent Mater. 24 (3): 299-307. doi: 10.1016/j.dental.2007.05.007. PMID: 17659331;
2. Rondoni D (2016). "Zirconia: Some practical aspects from the technologist's point of view". Int J Esthet Dent. 11 (2): 270-274. PMID: 27092353;
3. Manziuc MM, Gasparik C, Negucioiu M, Constantiniuc M, Burde A, Vlas I, et al. (2019). "Optical properties of translucent zirconia: A review of the literature". EuroBiotech J, 3 (1): 45-51. doi: 10.2478/ebtj-2019-0005;
4. Miranda PV, Rodrigues JA, Blay A, Shibli JA, Cassoni A (2015). "Surface alterations of zirconia and titanium substrates after Er, Cr: YSGG irradiation". Lasers Med Sci, 30 (1): 43-48. doI: 10.1007/s10103-013-1516-x. PMID: 24430726;
5. Özcan M, Valandro LF, Pereir, SM, Amaral R, Bottino MA, Pekkan G (2013). "Effect of surface conditioning modalities on the repair bond strength of resin composite to the zirconia core/veneering ceramic complex". J Adhes Dent, 15 (3): 207-210. doi: 10.3290/j.jad.a29717. PMID: 23700578;