Krstevska Aleksandra,Poser Maja,Zdraveski Filip
Abstract
This paper presents research about weldability between two dissimilar steels, martensitic steel P91 and 304H austenitic steel. Both materials are being preferred as a structural material for higher temperature applications due to their good mechanical properties at high temperatures. The mechanical properties at high temperature, such as tensile strength and creep resistance, are very important factors that ensure the application of materials. The P91 is modified martensitic Cr steel with higher amount of chromium which improves the higher temperature strength and molybdenum that increases creep resistance. On the other hand, the 304H represents advance austenitic stainless steel with controlled carbon content, which makes it ideal for applications requiring good mechanical properties at elevated temperatures. With increasing the demand of high efficiency in the power generation industry the high temperature applications usually require joints between advanced austenitic stainless steels and new class martensitic stainless steels in order to achieve the goal with the increased steam parameters. Therefore, this paper focuses on the weldability assessment between these two different steels and the characteristics of the weld metal.
Publisher
Centre for Evaluation in Education and Science (CEON/CEES)
Reference20 articles.
1. Viswanathan, R., Henry, J.F., Tanzosh, J. et al., (2005), U.S. program on materials technology for ultra-supercritical coal power plants. J. of Materi Eng and Perform 14, 281-292;
2. Iseda A, Kubota M et al, (1988), Application and properties of modified 9Cr-1Mo steel tubes and pipe for fossil-fired power plants, The Sumito Research (36);
3. Coussement C, de Witte M and de Backer T, (1993), Weldability and high temperature behavior of the modified 9%Cr steel grade P91 tube and pipe base materials and weldments, Materials Science;
4. ASME Boiler and Pressure Vessel Code, section IX;
5. C. Hurtado-Noreña, C.A. Danón, M.I. Luppo and P. Bruzzoni, (2015), Microstructural characterization of a P91 steel normalized and tempered at different temperatures, Structural materials for innovative nuclear systems;