Resistance of Austenitic Stainless Steels to Ductility-Dip Cracking: Mechanisms

Author:

YU PING, ,MORROW JUSTIN,KOU SINDO

Abstract

In Ni-based alloys, precipitates that form along grain boundaries (GBs) during terminal solidification have been shown to pin GBs and resist GB sliding, which can cause ductility-dip cracking (DDC). As a result, it is often suggested that the stainless steel skeletal/lacy  in a  matrix resists DDC because it pins GBs. In the present study, austenitic stainless steels 304, 316, 310, and 321 were quenched with liquid Wood’s metal (75˚C) during welding. Quenching captured the elevated-temperature micro-structure and simultaneously induced cracking, thus revealing the mechanisms of the resistance to DDC. In addition, DDC was much higher in 310 than 304, 316, and 321, which is consistent with results of conventional tests. Both 304 and 316 solidified as columnar  grains, with continuous  formed along GBs soon after solidification to resist DDC along the GBs. 321 solidified as equiaxed grains of  instead of columnar, and the tortuous GBs associated with equiaxed grains resisted DDC. 310, however, solidified as coarse, straight  grains with little  along the GBs, and solidification GBs migrated to become locally straight. The resulting GBs were long, straight, and naked, which is ideal for DDC. In 304, 316, or 321, skeletal/lacy  in a  matrix did not exist in the fusion zone near the mushy zone, where DDC occurs. This proved skeletal/lacy  cannot resist DDC as often suggested. Instead, the present study identified two new mechanisms of resistance to DDC: 1) formation of continuous or nearly continuous  along boundaries of columnar  grains and 2) solidification as equiaxed  grains.

Publisher

American Welding Society

Subject

Metals and Alloys,Mechanical Engineering,Mechanics of Materials

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3