Development of flux-cored wire of Fe – C – Si – Mn – Cr – W – V system with additives of carbon-fluorine-containing material and titanium

Abstract

The paper considers research of quality of the electric arc coating obtained using flux-cored wire of the Fe – C – Si – Mn – Cr – W – V system with additives of carbon-fluorine-containing material and titanium. The formation of an electric arc coating was carried out using an automatic arc welding machine ASAW-1250 with a new chromium-containing flux-cored wire on plates made of St3 steel. To exclude mixing of the deposited metal with the substrate steel, multilayer surfacing was conducted. The surfacing mode was calculated and refined experimentally. The authors studied the composition and properties of the surface of the electric arc coating after surfacing. As a substitute for amorphous carbon they used a carbon-fluorine-containing material (dust of gas purification of aluminum production). Surfacing was carried out under a flux made from slag produced by silicomanganese with a high content of sulfur. A regression analysis of influence of the deposited layer’s chemical composition on its hardness and wear rate was carried out and mathematical models of the investigated performance characteristics of the electric arc coating were obtained. With an increase in the content of chromium, tungsten, carbon and silicon, hardness of the deposited metal and its resistance to abrasive wear increase. The results of the conducted research make it possible to develop measures ensuring the required level of performance characteristics of the electric arc coating and can be used to make a forecast of hardness of the deposited layer and its wear resistance when the chemical composition of the metal changes, to predict the operational resistance of rolling rolls deposited with wires of the PP-Np-35V9Kh3SF type. Mathematical models of hardness of the deposited layer and its wear resistance help to clarify the mechanism of hardening and formation of protective properties of the surface layers of rolling rolls by means of electric arc coatings deposited with flux-cored wires.