Thermodynamic modeling of interphase distribution of chromium and boron in slags of AOD reduction period

Abstract

The paper presents the results of a thermodynamic modeling of the chromium and boron reduction from slags of reduction period of argon-oxygen decarburization (AOD) by a complex reducing agent containing silicon and aluminum. Using the simplex lattice method, an experiment planning matrix is constructed containing 16 compositions of the oxide system СаО – SiO2 – (3 – 6 %) В2О3 – 12 % Cr2O3 – 3 % Al2O3 – 8 % MgO of variable basicity 1.0 – 2.5. The results of thermodynamic modeling are graphically presented in form of dependence of equilibrium distribution of chromium and boron on the slag composition at temperatures of 1600 and 1700 °C. The constructed diagrams make it possible to quantify the influence of the temperature, basicity and B2O3 in the slag on equilibrium interphase distribution of chromium and boron. It is established that increasing the slag basicity from 1.0 to 2.5 improves the process of chromium reduction, but restores the boron stability. With an increase in B2O3 content in the slag, a slight deterioration of chromium reduction process occurs, while the boron content in the metal increases. With a simultaneous increase in basicity up to 2.5 and a decrease in boron oxide in the slag from 5 to 3 %, the interphase distribution coefficient of chromium is reduced to 1.5·10–3. Changing the process temperature from 1600 to 1700 °C does not have a negative effect on the process of chromium reduction, but worsens the boron reduction conditions. Based on analysis of the formed slag phases and thermodynamics of the reactions of their formation, it is established that chromium is mainly reduced by aliminum with only partial development of silicothermy. The residual silicon content reduces boron, thereby limiting its concentration in the metal. The results of high-temperature experiments showed high correspondence with the results of thermodynamic studies.