Cherkasova N. Yu.,Kuz’min R. I.,Antropova K. A.,Burkhinova N. Yu.
Abstract
The results of studies of aluminum oxide suspensions made with different CaO and SrO contents are presented. An increase in the pH level was recorded with an increase in the content of calcium and strontium oxides in aluminum oxide suspensions. With an increase in the CaO content from 0,45 to 2,25 mol. % and SrO from 0,42 to 2,14 mol. % exponential growth of dynamic viscosity is observed in Al2O3 suspensions. In the sintered materials, in the suspension of which CaO and SrO were introduced, there are reflexes of the compounds CaAl12O19 and SrAl12O19, respectively. These compounds have a lamellar structure. Ill. 4. Ref. 15. Tab. 2.
Publisher
National University of Science and Technology MISiS
Subject
Computer Networks and Communications,Hardware and Architecture,Software
Reference15 articles.
1. Tuan, W. H. Mechanical properties of Al2O3/ZrO2 composites / W. H. Tuan, R. Z. Chen, T. C. Wang [et al.] // J. Eur. Ceram. Soc. ― 2002. ― Vol. 22, № 16. ― P. 2827‒2833.
2. Burger, W. High strength and toughness alumina matrix composites by transformation toughening and «in situ» platelet reinforcement (ZPTA) ― the new generation of bioceramics / W. Burger, H. G. Richter // Key Eng. Mater. Trans. Tech. Publications. ― 2000. ― Vol. 192‒195. ― P. 545‒548.
3. Zemtsova, E. G. Formirovanie i mekhanicheskie svoistva alyumokislorodnoi keramiki na osnove mikro- i nanochastits oksida alyuminiya / E. G. Zemtsova, A. V. Monin, V. M. Smirnov [i dr.] // Fizicheskaya mezomekhanika. ― 2014. ― T. 17, № 6. ― S. 53‒58.
4. Myl'nikov, V. V. Issledovanie vliyaniya keramicheskikh materialov na rabotosposobnost' rezhushchego instrumenta / V. V. Myl'nikov, A. I. Pronin, E. A. Chernyshev // Trudy NGTU im. R. E. Alekseeva. ― 2011. ― T. 1. ― S. 227.
5. Kruzic, J. J. Crack blunting, crack bridging and resistance-curve fracture mechanics in dentin: effect of hydration / J. J. Kruzic, R. K. Nalla, J. H. Kinney, R. O. Ritchie // Biomaterials. Elsevier. ― 2003. ― Vol. 24, № 28. ― P. 5209‒5221.