Abstract
Ceramics based on barium aluminate with additives of iron (III) oxide and lithium hydroxide were obtained by solid-phase synthesis. It has been established that high-temperature treatment in an oxidizing medium contributes to the production of vacuum-dense samples that meet the «absolutely impermeable» tightness criterion, with a density of 3,75 g/cm3 , with a compressive strength limit of 597,1 MPa and a specific electrical conductivity in the range of 1,50·10‒7‒1,05·10‒4 Cm/ cm (at 90‒300 °C).
Publisher
National University of Science and Technology MISiS
Subject
Computer Networks and Communications,Hardware and Architecture,Software
Reference15 articles.
1. Vlasov, A. G. Vakuumnye kamery i vakuumnaya sistema betatronov 15‒25 Mev : elektronnye tsirkulyarnye uskoriteli / A. G. Vlasov // Izv. Tomskogo politekh. in-ta. ― 1957. ― T. 87. ― S. 301‒306.
2. Levin, A. M. Konstruktsionnye materialy i germetiki v vakuumnom priborostroenii / A. M. Levin. ― M. : Mashinostroenie, 1986. ― 60 s.
3. Goward, F. K. The design of electron synchrotrons / F. K. Goward, J. Lawson, J. Wilkin, R. Carrathers // Journal of the Institution of Electrical Engineers. ― 1950. ― Vol. 97. ― P. 320‒333.
4. Mohapatra, M. Effect of barium to aluminium ratio on phases leading to barium aluminates / M. Mohapatra, D. M. Pattanaik, S. Anand, R. P. Das // Ceram. Int. ― 2007. ― Vol. 33. ― P. 531–535. https://doi.org/10.1016/j.ceramint.2005.10.019.
5. Naoufal, D. Synthesis, structure and catalytic properties of Fe-substituted barium hexaaluminates / D. Naoufal, J. Millet, E. Garbowski [et al.] // Catalysis Letters. ― 1998. ― Vol. 54, № 3. ― P. 141–148. DOI:10.1023/A:1019004711495.