Effects of sintering temperature on the characteristics of aluminum oxide ceramics obtained without pressure using sintering additives of the Al2O3‒SiO2‒CaO system-Reference-Cited by-同舟云学术

Effects of sintering temperature on the characteristics of aluminum oxide ceramics obtained without pressure using sintering additives of the Al2O3‒SiO2‒CaO system

Published:2023-05-31 Issue:3 Volume: Page:32-42
ISSN:1683-4518
Container-title:NOVYE OGNEUPORY (NEW REFRACTORIES)
language:
Short-container-title:Nov. ogneup.

Author:

Ding Donghai,Guan Yue,Xiao Guoqing,Mao Zhaoyuan,Shi Xiaoqi,Gao Kaiqiang,Chong Xiaochuan,Luo Jiyuan,Lei Changkun

Abstract

The alumina ceramics with high compressive strength were prepared by pressureless sintering, and the kaolinite and calcium carbonate were added as Al2O3‒SiO2‒CaO sintering additives. The effects of sintering temperature on the volume shrinkage, bulk density, water absorption and compressive strength of the alumina ceramics were studied. The phase composition, crystal cell parameters, average grain size and microstructure of the ceramic were analyzed by XRD, SEM and EDS. The results show that the lattice tends to packed with the increase of sintering temperature. The bonding between grains is the most compact after sintering at 1700 ℃. The volume shrinkage increases with the increase of sintering temperature. The water absorption of alumina ceramics after sintering at 1700 °С reaches the minimum value of 0,06 %. The bulk density and compressive strength increase first and then decrease with the increase of sintering temperature. At 1700 ℃, optimized mechanical properties of alumina ceramics is obtained, with a bulk density of 3,80 g/cm3 and a compressive strength of 1323 MPa. Ill. 10. Ref. 41. Tab. 4.

Publisher

National University of Science and Technology MISiS

Subject

Computer Networks and Communications,Hardware and Architecture,Software

Reference41 articles.

1. Zhang, M. High-strength macro-porous alumina ceramics with regularly arranged pores produced by gel-casting and sacrificial template methods / M. Zhang, X. Li, M. Zhang [et al.] // J. Mater. Sci. ― 2019. ― Vol. 54, № 14. ― R. 10119‒10129.

2. Xing, Z. Effect of plasticizer on the fabrication and properties of alumina ceramic by stereolithography-based additive manufacturing / Z. Xing, W. Liu, Y. Chen, W. Li // Ceram. Int. ― 2018. ― Vol. 44, № 16. ― R. 19939‒19944.

3. De la Iglesia, P. G. Microstructural development and mechanical performance of mullite-alumina and hibonitealumina ceramics with controlled addition of a glass phase / P. G. De la Iglesia, O. García-Moreno, J. L. Menéndez [et al.] // Ceram. Int. ― 2018. ― Vol. 44, № 2. ― R. 2292‒2299.

4. Du, J. Fabricating a denser SiO2‒CaO co-doped 95 wt. % alumina ceramic to verify that small pores have no effect on the dielectric breakdown strength of alumina ceramics / J. Du, X. Yi, M. Li, K. Peng // J. Eur. Ceram. Soc. ― 2020. ― Vol. 40, № 15. ― R. 6218‒6222.

5. Li, H. The influence of sintering procedure and porosity on the properties of 3D printed alumina ceramic cores / H. Li, Y. Liu, P. Colombo [et al.] // Ceram. Int. ― 2021. ― Vol. 47, № 19. ― R. 27668‒27676.