Effect of radiotherapy on microhardness and surface morphology of pretreated primary teeth with silver diamine fluoride: an in vitro study

Author:

Das SimranORCID,Thosar Nilima,Luharia AnuragORCID,Mohanty Swaroop Narayan,Malviya NishiORCID,Ragit RutujaORCID

Abstract

Abstract Background: Children with head and neck cancer undergo radiation therapy, which has proved to be a successful treatment option. One of the common side effect of radiation therapy has been radiation induced caries. This is not as a result of the decreased salivary flow, but rather as a result of the direct impacts of these harmful rays on the enamel of the teeth. Silver diamine fluoride (SDF) is an effective remineralising agent for initial carious lesions and prevents demineralisation of the already deep carious agent. Various studies have also proved its effectiveness in improving the microhardness of the teeth. Hence, the objective of this study was to evaluate whether radiotherapy causes changes in the microhardness and surface morphology of enamel in primary teeth pretreated with SDF. Method: 22 primary teeth samples were divided into two groups with 11 samples in each group. The study group samples were pretreated with SDF and in the control group no pretreatment was done. Both groups were subjected to radiotherapy of 60 Gy radiation for a duration of 30 days. The samples were tested using the Vickers microhardness test and scanning electron microscope (SEM) analysis for surface morphological changes post radiotherapy. Results: It was found that there was a statistically significant difference (p<0.001) in mean microhardness values between the two groups. The mean microhardness of the SDF group (254.07 ± 35.84) was significantly higher that the control group (88.18 ± 6.79). SEM image of enamel of control teeth displayed loss of smooth homogeneous surface and more amorphous structures were seen which was very evident in comparison to the SDF group. Conclusion: Following radiation therapy, SDF application led to greater microhardness of the enamel surface and less morphological alteration in the surface enamel of primary teeth.

Publisher

F1000 Research Ltd

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3