Abstract
Abstract
The literature relatively lacks results and data related to the direct influence of physical ageing on the properties of polypropylene and natural rubber blend. So, the objective of this research is to study the influence of thermal and ultraviolet (UV) ageing on a natural rubber (NR) SMR-ω and polypropylene (PP) blend. This toughened blend is generally used for the fabrication of automobile parts and in the construction industry. The loading of the NR was 10, 20, 30, 40 and 50 wt %. The blends were prepared by calendering followed by melt extrusion and it was subjected to XRD (WAXS) analysis, mechanical testing, thermal and UV ageing, and optical microscopy (OM) observations. The results obtained by X-ray characterisation show that the adding of this kind of rubber does not affect the crystalline structure of the polypropylene matrix. Moreover, the adding of the rubber shows a decrease of the obtained material tensile strength and a valuable increase of the elongation at break. The shore A hardness decrease slightly as the percentage of the natural rubber increase. The optical microscopy indicates the apparition of cracks at the sample surfaces and debonded rubber domains from polypropylene matrix induced by UV and thermal ageing.
Publisher
Research Square Platform LLC
Reference37 articles.
1. Properties of Polypropylene/(Natural Rubber)/Organomontmorillonite Nanocomposites Prepared by Melt Blending”;Bendjaouahdou C;J. Vin. Add. Tech.,2011
2. Bendjaouahdou, C. “Ageing study and solvent resistance of a polypropylene and organoclay nanocomposite” Researchsquare, preprint, 1–16 (2023)
3. Bendjaouahdou C. “Etude structurale et thermodynamique de nanocomposite semi-cristallin polymer/argile” Phd Thesis, Biskra University, 2011
4. Mechanical and Morphological Properties of Polypropylene/Epoxidized Natural Rubber Blends at Various Mixing Ratio”;Mohamad N;Proced. Eng.,2013
5. ‘Effects of composition and dynamic vulcanization on the rheological properties of PP/NBR blends”;Hernandez M;Polym. Bull.,2003