The rhodium incorporated aluminide coating was produced by the rhodium electroplating (0.5 ?m thick layer) followed by the chemical vapor deposition process on the Inconel 713 superalloy. This coating is composed of the ?-NiAl phase. A part of nickel atoms was replaced by rhodium atoms in the ?-NiAl phase. The plain, rhodium and platinum incorporated aluminide coatings were oxidized at 1100 ?C under the atmospheric pressure. The oxidation kinetics of the rhodium and platinum incorporated aluminide coatings were similar, but different than oxidation kinetic of the plain coating. The ?-Al2O3 was the main product both in rhodium and platinum modified coatings after 360 h of oxidation. Moreover, the ?-Ni3Al phase, besides the ?-NiAl phase, was identified. The presence of 4 at. % rhodium in the coating provided similar oxidation resistance as the presence of 10-20 at. % platinum. Both rhodium and platinum incorporated aluminide coatings produced by the chemical vapor deposition process offer good oxidation protection of the Inconel 713 superalloy.
Publisher
National Library of Serbia
Subject
Materials Chemistry,Metals and Alloys,Mechanics of Materials,Geotechnical Engineering and Engineering Geology
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献