Spheroidization annealing of low carbon steel and its effects on the microstructure and mechanical properties of dual phase (DP) steel were studied. It was revealed that the reduction in strength and hardness of the quenched martensitic microstructure was much more pronounced compared to the fully annealed ferritic-pearlitic banded microstructure with spheroidizing time. This was related to the confinement of spheroidized carbide particles to distinct bands in the latter, and the uniform dispersion of carbides and high-temperature tempering of martensite in the former. During intercritical annealing of the spheroidized microstructures, the tendency to obtain martensite particles as discrete islands was observed. This, in turn, resulted in an inferior strength-ductility balance compared to the DP steel obtained from the intercritical annealing of martensite, which negated the usefulness of the spheroidized microstructures as the initial microstructures for the processing of DP steels.
Publisher
National Library of Serbia
Subject
Materials Chemistry,Metals and Alloys,Mechanics of Materials,Geotechnical Engineering and Engineering Geology
Cited by
10 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献