The Impact of nanoparticles (B4C-Al2O3) on mechanical, wear, fracture behavior and machining properties of formwork grade Al7075 composites

Author:

Prakash T. B.1,Gangadharappa M.2,Somashekar Santhosh3ORCID,Ravikumar M.4ORCID

Affiliation:

1. Department of Civil Engineering, B M S Evening College of Engineering, Bangalore, Karnataka, India

2. Graphite India Limited, Bangalore, Karnataka, India

3. Department of Mechanical Engineering, B M S College of Engineering, Bangalore, Karnataka, India

4. Dept. of Mechanical Engineering, B M S College of Engineering, Karnataka 560019, India

Abstract

This study explores how ageing temperature and the volume percentage of Al2O3+B4C nanoparticles influence the machinability and hardness of stir-cast Al-7075 Metal Matrix Composite (MMC). Using liquid metallurgy techniques, hybrid materials were created by reinforcing Al7075 metal matrix with varying weight percentages of nanosized B4C (1.5%, 3%, and 4.5%) and Al2O3 (1%, 1.5%, and 2%). After fabrication, the samples were subjected to five-hour ageing process at temperatures of 100, 120, and 140 degrees Celsius, followed by cooling to ambient temperature (27 degrees Celsius). Hybrid nano composites that had been heat treated were tested for wear, tensile strength, and hardness. Results shows that, the addition of nanoparticles and heat treatment considerably improves the tensile strength, hardness, and wear resistance of hybrid composites by 3%, 17%, and 10%, respectively, for samples reinforced with 4.5% B4C + 2% Al2O3. SEM analysis was used to investigate the type of wear and the tensile fracture mode of nano composite samples by analyzing the wornout surface and the surface where tensile fracture occurred. Machinability was assessed using L27 orthogonal array tests, focusing on three key process parameters: feed rate (0.1 mm/min), depth of cut (0.2 mm/min), and spindle speed (1000 rpm). Outcomes show that, increasing the wt. % of nano-Al2O3/B4C leads to higher machining force and surface roughness (Ra) of MMCs. Conversely, higher ageing temperatures result in decreased machining force and surface roughness. Optimal surface roughness and machining force were achieved with 1% Al2O3 + 1.5% B4C and an ageing temperature of 140°C. These findings offer valuable insights into the ease of machining of composite metal alloys, emphasizing the importance of parameter selection and optimization for desired machining outcomes.

Publisher

Gruppo Italiano Frattura

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3