Affiliation:
1. Research Division of Green Function Materials and Equipment , School of Mechanical and Automotive Engineering, South China University of Technology, Guangzhou , PRC
Abstract
Abstract
The effects of graphene nano-platelets (GNPs) content on melt flow behavior and flexural properties of reinforced polypropylene (PP) composites were investigated. The results showed that both the flexural modulus and strength at room temperature increased when GNPs weight fraction was lower than 0.4 wt.%, and then decreased with increasing GNPs weight fraction. During the melt flow of the PP composites in capillary extrusion within temperatures ranging from 180 to 230 °C and in apparent shear rates varying from 100 to 4 000 s−1, the melt shear flow followed the power law relationship, and the dependence of the melt shear viscosity on temperature obeyed the Arrhenius equation. The correlation between the melt shear viscosity and GNPs weight fraction was approximately linear under the given test conditions.
Subject
Materials Chemistry,Industrial and Manufacturing Engineering,Polymers and Plastics,General Chemical Engineering
Cited by
5 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献