Abstract
The crush test and acid resistance of microsphere narrow fractions with average diameter dav of 5, 8 and 25 μm of the SiO2–Al2O3–FeO system and with dav of 4 and 10 μm the CaO–SiO2–Al2O3– FeO system separated from fly ash from pulverized combustion of Ekibastuz and Irsha-Borodinsky coals were studied. It has been established that all investigated ash fractions of both raw materials are characterized by high strength: microspheres of a larger narrow fraction with dav = 25 μ m a re not destroyed by compressive loading at pressures up to 51.7 MPa, dispersed narrow fractions of microspheres with dav ≤ 10 μm – up to 68.9 MPa. Microsphere narrow fractions with aluminosilicate composition have satisfactory acid resistance; the weight loss after treatment with 15 % hydrochloric acid at 65 °C for 30 minutes was 10–15 wt. %
Publisher
Siberian Federal University
Subject
General Chemical Engineering,General Chemistry
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献