Abstract
Abstract
A simple, lightweight, and easy to develop Single Jersey Wearable Tribo-Electric Nano Generators (SJ-WTENG) were constructed using Cotton and Acrylic fabrics (Triboelectric series materials). Fabrics were also coated with Maghemite (γ-Fe2O3) nanoparticles (13 nm) to increase the electrical conductance of the samples. Compression and Vertical contact-separation modes were adopted for studying the performance of the developed samples. Along with a Single WTENG sample, the outputs of two samples connected in series were also measured. To study the effect of developed Maghemite (γ-Fe2O3) nanoparticle coating, non-coated fabrics WTENGs were also constructed and tested. The maximum voltage reached with the Maghemite (γ-Fe2O3) nanoparticle-coated SJ-WTENG samples was a time-varying signal of 7.68 volts peak to peak volts with an approximate frequency of 50.5 Hertz. A shotky diode-based full bridge rectifier was used to get the DC voltage. The rectified DC signal was observed to be 5 volts which was enough to light up an LED with a threshold voltage of 1.7 volts DC as well as charge 3.7 volts, 3.6Ah Li-ion battery pack. Results confirmed that the application of Maghemite (γ-Fe2O3) nanoparticles was useful in augmenting the output of the proposed SJ-WTENG design. The proposed system can be used to power the battery powered IOT (Internet of Things) devices, widely used in medical and body sensor network applications.