Battery safety calls for solid state batteries and how to prepare solid electrolytes with excellent performance are of significant importance. In this study, hybrid solid electrolytes combined with organic PVDF-HFP and inorganic active fillers are studied. The modified active fillers of Li7−x−3y
Al
y
La3Zr2–x
Ta
x
O12 are obtained by co-element doping with Al and Ta when LLZO is synthesized by calcination. And an high room temperature ionic conductivity of 5.357 × 10−4 S cm−1 is exhibited by ATLLZO ceramic sheet. The composite solid electrolyte PVDF-HFP/LiTFSI/ATLLZO (PHL-ATLLZO) is prepared by solution casting method, and its electrochemical properties are investigated. The results show that when the contents of lithium salt LiTFSI and active filler ATLLZO are controlled at 40 wt% and 10%, respectively, the ionic conductivity of the resulting composite solid electrolyte is as high as 2.686 × 10−4 S cm−1 at room temperature, and a wide electrochemical window of 4.75 V is exhibited. The LiFePO4/PHL-ATLLZO/Li all-solid-state battery assembled based on the composite solid-state electrolyte exhibits excellent cycling stability at room temperature. The cell assembled by casting the composite solid-state electrolyte on the cathode surface shows a discharge specific capacity of 134.3 mAh g−1 and 96.2% capacity retention after 100 cycles at 0.2 C. The prepared composite solid-state electrolyte demonstrates excellent electrochemical performance.
Funder
Youth Program of Hunan Provincial Science Foundation
National Natural Science Foundation of China
Subject
Electrical and Electronic Engineering,Mechanical Engineering,Mechanics of Materials,General Materials Science,General Chemistry,Bioengineering
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献