Interface modification for efficient carbon-electrode CsPbI2Br perovskite solar cells using ionic liquid

Abstract

Abstract All-inorganic CsPbI2Br, as a promising photovoltaic (PV) material, have attracted extensive research attention in society for its outstanding thermal stability and appropriate trade-offs. Carbon-based perovskite solar cells (C-PSCs) without hole transporting layer (HTL) have shown great potential in terms of cost-effectiveness and stability. However, the inevitable defects on the surface of CsPbI2Br films severely hampers the development of high-efficiency CsPbI2Br C-PSCs. Surface engineering has emerged an effective approach to overcome this challenge. Herein, 1-decyl-3-methylimidazolium tetrafluoroborate (DMTT) ionic liquid was introduced between CsPbI2Br and carbon electrode to reduce non-recombination of charges, decrease defect states, minimize the energy-level mismatch, and greatly enhance the device stability. As a result, the HTL-free CsPbI2Br C-PSCs combined with DMTT as an interface modification achieved a higher power conversion efficiency (PCE) of 12.47% than that of the control devices with a PCE of 11.32%. Furthermore, without any encapsulation, the DMTT-optimized C-PSC remained approximately 84% of its initial PCE after over 700 h under room temperature and 25% relative humidity (RH) conditions. Additionally, when exposed to a temperature of 65 °C for over 400 h, the device still retained 74% of the initial PCE, demonstrating its thermal stability.