Mesoporous γ-Al2O3 nanofibers with high pore volume and uniform pore size distributions were successfully synthesized via a template-free method in a membrane dispersion microreactor followed by calcination. The effects of crystal temperature, pH values, continuous phase concentration and washing solvent on the γ-Al2O3 nanofibers were carefully studied. The results showed that the as-obtained γ-Al2O3 nanofibers showed a length of 40–60 nm and a width of 3.2–3.4 nm, which were attributed to the high microscopic mixing rate in the membrane dispersion microreactor. Moreover, the precursors of γ-Al2O3 nanofibers treated with deionized water and mixed deionized water/alcohol solution had high pore volumes, reaching to 1.60 ml g−1 and 2.00 ml g−1, respectively. Furthermore, the adsorption performance of γ-Al2O3 nanofibers with high pore volumes was also investigated. These fibers showed an excellent adsorption capacity of 1323.68 mg g−1 for the removal of Congo red from aqueous solution, thereby indicating their potential for applications in adsorption and other related areas.
Subject
Electrical and Electronic Engineering,Mechanical Engineering,Mechanics of Materials,General Materials Science,General Chemistry,Bioengineering
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献