Abstract
Abstract
This research deals with the process of deforming cadmium metal with silver metal directly by planting pieces of silver cylindrical shape on the surface of the target material of cadmium and by using the DC reactive magnetron sputtering technique deposit on a glass substrate. The flow rate of argon and oxygen gases fixed to (90 and 10) sccm and sputter time was 120 min per model (0, 1, 2 and 3) Ag chips, the current of sputtering and the voltage of sputtering were kept within the process of deposition at 18 mA and 1300 V, The temperature of substrate had been set at 150°C. The structural properties showed that all films prepared have a polycrystalline diffraction pattern with a predominant orientation of the plane (111) and an increase in the size of the crystal from 17.17 nm to 19.30 nm with the number increases of chips above the surface of target material, and the growing of spherical nanoparticles with a diameter ranges from (25- 40) nm
Reference24 articles.
1. Mechanistic Basis of Antimicrobial Actions of Silver Nanoparticles;Dakal;Front. Microbiol.,2016
2. Silver nanoparticles as potential antibacterial agents;Franci;Molecules,2015
3. A Review of Silver Nanoparticles: Synthesis Methods, Properties and Applications;Natsuki;Int. J. Mater. Sci. Appl.,2015
4. Biosynthesis, purification and characterization of silver nanoparticles using Escherichia coli;Gurunathan;Colloids Surf. B. Biointerfaces,2009
5. Silver nanoparticles: Synthesis, characterization, properties, applications, and therapeutic approaches;Zhang;Int. J. Mol. Sci.,2016