Neustroev E P,Prokopyev A R,Semenov S O,Popov V I,Protopopov F F,Andreev A S,Savvinova N A,Lukin E S
Abstract
Abstract
In the work, the properties of graphene oxide processed in methane plasma and plasma of a mixture of methane and nitrogen and subjected to subsequent annealing at T = 650 ° C in an argon atmosphere are investigated. It is shown that during plasma treatment, the hydrogenated amorphous carbon film is deposited on the surface of the exhaust gas. During heat treatment, a significant part of this film is removed, another part of the carbon atoms participates in the formation of bonds with the structure of the exhaust gas. This process leads to a decrease in the density of defects introduced by the plasma. The inclusion of nitrogen in methane plasma leads to n or p doping depending on the plasma power level. This effect is explained by the predominant formation of graphite and pyridine nitrogen configurations, which are donor centers in structures with fewer defects. At a high density of defects, pyrrole nitrogen structures, which are acceptor centers, are mainly introduced.
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献