Effect of loading frequency on corrosion fatigue crack growth rate of 7N01 aluminum alloy

Author:

Yu Yangyang,Sun Weiguang,Tong Dihua

Abstract

Abstract The fatigue damage of engineering structures is mostly caused by cyclic stress and external environmental factors. Therefore, the study of corrosion fatigue crack propagation is of great significance to the safety and durability of structures. The effects of different loading frequencies (10Hz, 1Hz and 0.1Hz) on fatigue crack growth rate of 7N01 aluminum alloy in humid air were studied by using load control method. The results show that the corrosion fatigue crack growth rate is basically the same at 10Hz and 1Hz, When the loading frequency decreases to 0.1Hz, the corrosion fatigue crack growth rate is slightly higher than 10Hz and 1Hz.

Publisher

IOP Publishing

Subject

General Medicine

Reference6 articles.

1. Spectrum Crack Growth Prediction Method Based on Crack Surface Displacement and Contact Analyses, Fatigue Crack Growth Under Spectrum Loads;Dill,1976

2. Effect of Fighter Attack Spectrum on Crack Growth;Dill,1977

3. Effect of Temperature on Stress Corrosion Cracking of 300M Steel;Ryder;Journal of Testing and Evaluation,1978

4. Correlation Between Sustained-Load and Fatigue Crack Growth in High Strength Steels;Wei;Materials Research and Standards,1969

5. Summary of Landing Gear Initial Flaws;Fujimoto,1977

Cited by 3 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3