Fajobi M A,Loto R T,Oluwole O O
Abstract
Abstract
The electrochemical reaction response of austenitic 316L stainless steel and carbon steel was examined through weight loss analysis in 1M, 2M and 3M of HCl acid. The results show that austenitic 316L has high corrosion resistance than carbon steel for the test analyzed with the lowest corrosion rate of 0.0018mm/y at 1M of HCl and highest at 0.0053mm/y when compared with carbon steel which has the lowest corrosion rate of 0.0003mm/y for 1M of HCl and highest at 0.0013 mm/y of 3M of HCl solution all at ambient temperature conditions. General corrosion was displayed on the surface of the carbon steel but austenitic 316L was not affected due to the presence of chromium alloy and other alloying elements.
Reference16 articles.
1. Refining of crude and its corrosion control using distributed control system;Ramraj;World Sci. Eng. Acad. Soc. Trans Syst. Control,2014
2. Inhibitive Performance of Ibuprofen Drug on Mild Steel in 0.5 M of H 2SO4 Acid;Fajobi;J. Bio-Tribo-Corrosion,2019
3. Biocorrosion of oil and gas field equipment and chemical methods for its suppression;Moiseeva;Prot. Met.,2005
4. Cost of corrosion in the United States;Koch,2005
Cited by
5 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献