Air Content in Fresh Air-Entraining Cement Mortars

Abstract

Abstract The durability of a cement composite is the most important criterion for assessing this material. However, due to the durability of the cement composite, its frost resistance is an important property. In order to ensure concrete frost resistance, the European standard PN-EN 206-1: 2013 requires its aeration at the level of 4 - 7%. The Committee 201 of the American Concrete Institute (ACI) also requires the use of an air-entraining admixture in concretes exposed to frost damage. The amount of air-entraining admixture is significantly influenced by the composition of the cement used. In order to minimize the problems with obtaining frostresistant concrete, an attempt was made to create air-entraining cements. This article presents the effect of the amount and type of dosing of air-entraining admixtures (natural and synthetic) on the air content in fresh air-entraining cement mortars. The test cements used also differed in the production method: joint mixing of components and joint grinding of components. Based on the research, a lot of valuable information was obtained related to the influence of the preparation of air-entraining cements on the air content in the mortar, e.g. mortars with mixed cement with natural air-entraining admixture have a higher air content. The air content is higher in the cement co-ground with natural air-entraining admixture. A synthetic air entraining admixture added separately to mixed cements with silica fly ash and ground granulated blast furnace slag increases air entrainment in mortars. The synthetic air-entraining admixture added separately to co-milled cements causes an increase in air entrainment in the mortars, except for those containing cement with ground granular blast furnace slag.