Author:
Wahyudi B,Muljani S,Alfan M A,Zukhrufiansyah A R
Abstract
Abstract
The β-tri-calcium phosphate (β-TCP) is a calcium phosphate compound also called whitlockite. This form is more widely used because of its chemical stability, high mechanical strength and better bio-sorption when compared with α-Tri-calcium-phosphate. β-tri-calcium phosphate in this study was obtained from reactions of calcium oxide and phosphoric acid by precipitation method. Precipitation at 50 °C while sintering at 600, 700, 800, 900, and 1000 °C, in the sintering range of 1-5 hours. Green mussel shell has calcium carbonate (CaCO3) content 60-70 % then calcined at 1000 °C to get calcium oxide (CaO). The result shows that β-tri-calcium phosphate optimum reached of 72% at sintering temperature 1000 °C for 5 hr sintering time. The crystal structure of β-tri-calcium phosphate formed is a rhombohedral crystal with a Ca / P ratio mole of 2.72
Subject
General Physics and Astronomy
Reference21 articles.
1. Preparation of Calcium Phosphate with Oyster Shells;Onoda;Nat Res,2012
2. α-Tricalcium phosphate: Synthesis, properties and biomedical applications;Carrodeguas;Act Bio,2012
3. Preparation of a biphasic calcium phosphate from Ca(H2PO4)2·H2O and CaCO3;Jaw;J Therm Ana and Calor,2006
4. The role of chemical composition of monetite on synthesis and properties of α-tricalcium phosphate;Duncan;Mater Sci Eng C Mater Biol,2014
5. Mechanical Properties and In Vitro Bioactivity of β-Tri Calcium Phosphate, Merwinite Nanocomposites;Abbasi,2012
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献