Production of corundum armored ceramics

Abstract

Abstract The purpose of this study was to develop the compositions and technology of corundum armored ceramics with high ballistic characteristics based on aluminum oxide with an α-Al2O3 content of more than 99 wt.%. The results of the study of the physicochemical processes of obtaining corundum ceramics modified with complex additives consisting of magnesium - aluminosilicate eutectic mixture and oxides of magnesium, yttrium, titanium, zirconium are presented. The introduction of complex additives into the composition of corundum ceramics provides a significant reduction (100-150°C) of the sintering temperature of the product. In this case, additives of yttrium and zirconium oxides contribute to the formation of a uniform-grained microstructure of ceramics, and in the case of adding titanium oxide, a collective recrystallization of corundum grains is noted. The use of small additives (0.3-0.5 wt.%) of magnesium and yttrium oxides together with a eutectic mixture in the compositions of corundum ceramics based on high-quality alumina contributes to the formation of a uniform-grained, dense structure of the material and giving it a high level of physical and mechanical properties as a result of directional the action of each component of the additive on the physicochemical processes of phase formation of the crystalline matrix. A model idea of the mechanism of action of additives on the formation of the microstructure of ceramics during stage-by-stage heating from 1350 to 1650°C in the sintering mode of products is presented. The developed compositions and technologies of corundum armored ceramics have a production focus and implementation in practice.