Preparation and characterization of graphene nanosheet doped with silver nanoparticles

Abstract

Abstract Simple process (exploding wire technique) was used to Prepared sliver nanoparticles (AgNPs). The graphene sheet was added to AgNPs with different concentrations (0.002g/ml and 0.01g/ml). well dispersion of AgNPs are achieved by simple chemistry process. The samples were characterized by ultraviolet-visible spectroscopy (UV-Vis), x-ray diffraction (XRD), atomic force microscopy (AFM) and Field emission scanning electron microscope (FESEM). The results showed a wide band absorption of AgNPs-graphene (AgNPs-GN) extended from VU to IR region, surface plasmon resonance (SPR) absorption peak position for the AgNPs at (350-600) nm, XRD confirmed the clear distribution of the peaks attributed to polycrystalline for AgNPs appeared at 20=38.14°, 44.27°, 64.33, and 77.37° respectively and AgNPs-GN at 2θ=26.51° and 54.65°. The AFM showed that AgNPs have uniformly distribution on the surface of graphene sheet. The average size of AgNPs was confirmed by around (50-80) nm by FESEM and the AgNPs-GN have average particle size (20-40) nm. The AgNPs-GN could become prominent candidate for optoelectronic applications.