Chen Ting Ting,Shi Yong Jun
Abstract
Abstract
Ti-6Al-4V alloys are popular structural materials for the production of critical components. However, its poor surface properties, such as friction and high-temperature oxidation, further limit its application scope. Ti-Al-Cr-Nb coating was deposited on the Ti-6Al-4V alloy through laser cladding. The tendency of cracks was low when the laser energy density was 14.33-8.19 kw · s · cm
−2, the corresponding effective process parameters were the laser power of 1600-1800 W matching the scanning speed of 4-6 mm/s. Due to the formation of Ti3Al intermetallic compound phase, and the lattice distortion caused by adding a small amount of Cr and Nb playing a role in solid solution strengthening, average vickers hardness of the coating was about 583.3 HV0.1, which was about 1.7 times that of the substrate.
Subject
Computer Science Applications,History,Education
Reference13 articles.
1. Research progress on laser surface modification of titanium alloys;Tian;Appl Surf Sci,2005
2. Microstructure and wear resistance of laser clad composite coating on TC4 titaniumal alloy surface;Liu;Heat Treatment of Metals,2015
3. Surface improvement and biocompatibility of TiAl24Nb10 intermetallic alloy using rf plasma nitriding;Abd Ei-Rahman;Appl Surf Sci,2007
4. Tribological properties oftitanium aluminides coatings produced on pure Ti by laser surface alloying;Guo;Surf Coat Technol,2008
5. Path selection and quality analysis of laser clad CoCrMo strengthened coating on titanium alloy surface;Shang;Heat Treatment of Metals,2021