Abstract
Abstract
Ceramic injection moulding (CIM) is a near net shape process to produce smaller and intricate parts at a competitive cost. However, fine particle size (nano scale) used for such injection moulding process generally leads to agglomeration, higher binder content and critical dimensional shrinkage which results in defects on the sintered components. This study extensively investigates the characteristics of Yttria Stabilized Zirconia (YSZ) for CIM process. YSZ parts were moulded by CIM process that utilized a multi-component binder system using palm stearin (PS) and polyethylene (PE) in 60:40 (vol %) ratio. The powders were characterized using particle size analyzer, pycnometer density and scanning electron microscopic (SEM). The binders were characterized by the pycnometer density, differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). Powders loading were choosen by the critical powder volume percentage (CPVP) through oil absorption test. YSZ powder was mixed with the binders at different powder loadings ranging from 58 to 60 vol% based on CPVP. The parts were injected moulded, thermal debound, pre-sintered and sintered. The microstructure, green strength and hardness of the sintered part at different powder loadings were investigated. A large porous region was clearly observed at 58 vol% compared to 60 vol%. All samples were sintered at 1350°C, with the highest green strength and hardness were 13MPa and 357.42 HV respectively was given by the sintered part at powder loading of 60 vol.
Subject
General Physics and Astronomy
Reference19 articles.
1. Micro powder injection moulding-challenges and opportunities;Petzoldt;Powder Injection Moulding International,2008
2. Keupayaan Pemprosesan Ytria Zirkonia Terstabil Bersaiz Nano Dengan Bahan Pengikat Berasaskan Stearin Sawit Dalam Pengacuan Suntikan Serbuk Mikro;Mohd Foudzi,2011
3. Microstructural Properties of Yttria Stabilized Zirconia (YSZ) Prepared by Ceramic Injection Moulding (CIM);Zainudin,2019
4. Effect of sintering parameters on physical and mechanical properties of powder injection moulded stainless steel-hydroxyapatite composite;Ramli;PLoS ONE,2018
5. Sintering behavior and mechanical properties of injection-molded zirconia powder;Lee;Ceramics International,2004
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献